Abstract
Fiber textures of drawn wires of Al-Zn alloys containing precipitates were studied mainly by X-ray methods. In supersaturated solid solution the wire texture was a double fiber texture with [100]and [111]. It was considered that a phase precipitates were rotated with matrix, while they were deformed. And then the matrix containing stable precipitates (Zn) had [100] and [111] textures. The intense spots, corresponding to [111] fiber texture of matrix, in the Debye rings of (002)p and (101)p planes of precipitates were clearly observed. But, on the other hand, spots, corresponding to [100] fiber texture of matrix, shown the prefered orientation of precipitates in (002)p Debye ring were very weak and brodening.
Publication Title
Memoirs of the School of Engineering, Okayama University
Published Date
1971-09-01
Volume
volume6
Issue
issue1
Publisher
岡山大学工学部
Publisher Alternative
School of Engineering, Okayama University
Start Page
27
End Page
31
ISSN
0475-0071
NCID
AA00733903
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
英語
File Version
publisher
NAID
Eprints Journal Name
mfe