|| Fiber textures of drawn wires of Al-Zn alloys containing precipitates were studied mainly by X-ray methods. In supersaturated solid solution the wire texture was a double fiber texture with and . It was considered that a phase precipitates were rotated with matrix, while they were deformed. And then the matrix containing stable precipitates (Zn) had  and  textures. The intense spots, corresponding to  fiber texture of matrix, in the Debye rings of (002)p and (101)p planes of precipitates were clearly observed. But, on the other hand, spots, corresponding to  fiber texture of matrix, shown the prefered orientation of precipitates in (002)p Debye ring were very weak and brodening.