JaLCDOI 10.18926/15636
FullText URL Mem_Sch_Eng_OU_6_27.pdf
Author Ohta Mutsuo| Hashimoto Fumio| Maeda Hironobu|
Abstract Fiber textures of drawn wires of Al-Zn alloys containing precipitates were studied mainly by X-ray methods. In supersaturated solid solution the wire texture was a double fiber texture with [100]and [111]. It was considered that a phase precipitates were rotated with matrix, while they were deformed. And then the matrix containing stable precipitates (Zn) had [100] and [111] textures. The intense spots, corresponding to [111] fiber texture of matrix, in the Debye rings of (002)p and (101)p planes of precipitates were clearly observed. But, on the other hand, spots, corresponding to [100] fiber texture of matrix, shown the prefered orientation of precipitates in (002)p Debye ring were very weak and brodening.
Publication Title Memoirs of the School of Engineering, Okayama University
Published Date 1971-09-01
Volume volume6
Issue issue1
Start Page 27
End Page 31
ISSN 0475-0071
language 英語
File Version publisher
NAID 120002307980