Corrosion Behavior of Silica Glass in High-Pressure Water Vapor at 300℃
FullText URL
Author
Oda, Kohei
Takata, Katsumi
Yoshio, Tetsuo
Abstract
Corrosion behavior of silica glass was investigated in high-pressure water vapor and water at 300℃. A linear weight loss in water vapor and a parabolic weight loss in water were observed. The weight loss for the former was larger than that for the later. The fracture strength of the corroded silica glass increased with the content of molecular water in the glass. The strength reduction was observed for the corroded silica glass after dehydration at 400℃ for 1 day.
Keywords
Autoclave
FT-IR
Fracture strength
Hydrothermal treatment
Dehydration
Publication Title
岡山大学環境理工学部研究報告
Published Date
1997-01-10
Volume
volume2
Issue
issue1
Publisher
岡山大学環境理工学部
Publisher Alternative
Faculty of Environmental Science and Technology, Okayama University
Start Page
131
End Page
135
ISSN
1341-9099
NCID
AN10529213
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
日本語
File Version
publisher
NAID
Eprints Journal Name
fest