尾坂 明義 Department of Bioengineering Science
Kobayashi Keizo Department of Bioengineering Science
早川 聡 Department of Bioengineering Science
大槻 主税 Department of Bioengineering Science
抄録
The thermal expansion coefficient of some bioactive glasses in the system CaO-SiO(2)-B(2)O(3) were adjusted to be similar to that of titanium by controlling the composition. A glass of composition 45CaO・30SiO(2)・25B(2)O(3) was selected among those as the enameling glass. A slurry was prepared by mixing the glass powder and ethanal to be developed on titanium and heated at 740℃ for 30 min. Thus treated specimen was soaked in a simulated body fluid (Kokubo solutiion). FT-IR reflection and thin film X-ray diffraction analyses indicated apatite formation on the glass coating layer within 12 h of soaking in the fluid. Thus titanium could be provided with bioactivity due to the enameling.
発行日
1997-03-28
出版物タイトル
Memoirs of the Faculty of Engineering, Okayama University
出版物タイトル(別表記)
岡山大学工学部紀要
31巻
2号
出版者
Faculty of Engineering, Okayama University
出版者(別表記)
岡山大学工学部
開始ページ
45
終了ページ
51
ISSN
0475-0071
NCID
AA10699856
資料タイプ
紀要論文
言語
English
論文のバージョン
publisher
査読
無し
Eprints Journal Name
mfe