Ohta Mutsuo Department of Industrial Science
Hashimoto Fumio Department of Electronics
Maeda Hironobu Department of Industrial Science
抄録
Fiber textures of drawn wires of Al-Zn alloys containing precipitates were studied mainly by X-ray methods. In supersaturated solid solution the wire texture was a double fiber texture with [100]and [111]. It was considered that a phase precipitates were rotated with matrix, while they were deformed. And then the matrix containing stable precipitates (Zn) had [100] and [111] textures. The intense spots, corresponding to [111] fiber texture of matrix, in the Debye rings of (002)p and (101)p planes of precipitates were clearly observed. But, on the other hand, spots, corresponding to [100] fiber texture of matrix, shown the prefered orientation of precipitates in (002)p Debye ring were very weak and brodening.
出版物タイトル
Memoirs of the School of Engineering, Okayama University
発行日
1971-09-01
6巻
1号
出版者
岡山大学工学部
出版者(別表記)
School of Engineering, Okayama University
開始ページ
27
終了ページ
31
ISSN
0475-0071
NCID
AA00733903
資料タイプ
紀要論文
OAI-PMH Set
岡山大学
言語
English
論文のバージョン
publisher
NAID
Eprints Journal Name
mfe